Abstract:
The rare earth-doped CuMnOx catalysts were prepared by co-precipitation method. The CuMnOx catalyst was doped with (1.5 wt.%) CeOx, (1.0 wt.%) AgOx, and (0.5 wt.%) of AuOx by the dry deposition
method. After the precipitation, filtration, and washing process, drying the sample at 110 oC for 16 hr
in an oven and calcined at 300 oC temperature for 2 h in the furnace at stagnant air calcination condition. The influence of doping on the structural properties of the catalyst has enhanced the activity of
the catalyst for CO oxidation. The doping of noble metals was not affected the crystal structure of the
CuMnOx catalyst but changed the planar spacing, adsorption performance, and reaction performance.
The catalysts were characterized by Brunauer-Emmett-Teller (BET) surface are, Scanning Electron
Microscope Energy Dispersive X-ray (SEM-EDX), X-Ray Diffraction (XRD), and Fourier Transform Infra Red (FTIR) techniques. The results showed that doping metal oxides (AgOx, AuOx, and CeOx) into
CuMnOx catalyst can enhance the CO adsorption ability of the catalyst which was confirmed by different types of characterization technique. Copyright © 2017 BCREC Group. All rights reserved