Abstract:
Mott-Hubbard anti-ferromagnetic insulator, NiO shows p-type semiconducting behaviour due to vacancy at Ni2+ site in its bunsenite structure. We report the modification of structural and magnetic order in NiO on Fe doping. NiO samples at different Fe concentrations in the range 0 to 5 at.% have been prepared by chemical co-precipitation and post thermal decomposition method. Both structural and magnetic characterization reveal that with increasing Fe doping concentration, NiO evolves as a magnetically inhomogeneous state out of the parent homogeneous antiferromagnetic state. In addition, structural inhomogeneity was also observed with Fe precipitating to γ-Fe 2O3 phase, the signature of which could be clearly seen for Fe content beyond 2 at.%. At lower Fe content however, some amount of Fe occupies lattice and interstitial sites in the NiO matrix and drive the latter to acquire ferromagnetic ordering, which was evident from a clear hysteresis loop at 300 K.